求翻译：随着交联度的降低，树脂的胺基交换量增大；交联度越低（摩尔交联度低于10%），DMAEMA的共聚成球性能越差，甚至得不到球形树脂。致孔剂对树脂制备亦有很大影响，在无致孔剂时，DMAEMA与TRIM共聚时，交联度低于20%（摩尔交联度）成球效果就变差；良溶剂甲苯、邻苯二甲酸二甲脂为致孔剂得到凝胶型树脂；甲苯－液腊混合致孔剂得到大孔型树脂。是什么意思？

With the crosslinking degree of reduction, amino resin exchange capacity increases; the lower the degree of crosslinking (the molar degree of crosslinking is less than 10%), dmaema copolymer into a ball the worse performance, even without spherical resin. Porogen preparation also have a great impact

As to the degree of reduction, the amine-based resin exchange; the higher the degree the lower (Moore to the low 10 per cent) in the copolymer, DMAEMA performance into a ball, do not even have ball resin. The hole is also produced in the resin have a big impact, in a hole, line, and TRIM DMAEMA came

Along with degree of cross linking depression, the resin amidogen exchange quantity increases; The degree of cross linking is lower (a mole of degree of cross linking to be lower than 10%), the DMAEMA copolymerization becomes the ball performance to be worse, even cannot obtain the sphere resin.Send

Crosslinking degree of reduction, amino resin exchange capacity increase; lower the cross-linking degree (Republic of Crosslinking degree lower than 10%), pelletizing properties of copolymers of DMAEMA worse, even are not spherical resin. To hole agent on resin preparation also has is large effect,