求翻译：Sato 等，suggested the possibility of constitutional liquation as the mechanism for the formation of the eutectic structure during 搅拌摩擦焊 of AA1050 to AZ61. On the other hand, Gerlich et al.27 conducted 搅拌摩擦点焊 of AA6111 to AZ91 and determined that the peak temperature in the vicinity of the tool rapidly reached the a-Mg+A是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Sato 等，suggested the possibility of constitutional liquation as the mechanism for the formation of the eutectic structure during 搅拌摩擦焊 of AA1050 to AZ61. On the other hand, Gerlich et al.27 conducted 搅拌摩擦点焊 of AA6111 to AZ91 and determined that the peak temperature in the vicinity of the tool rapidly reached the a-Mg+A
问题补充： |
|
2013-05-23 12:21:38
佐藤等共晶结构的形成机制，建议在搅拌摩擦焊的aa1050 AZ61宪法液化的可能性。另一方面，gerlich等al.27进行搅拌摩擦点焊的aa6111 AZ91和决心，在附近的工具峰值温度迅速达到一毫克+ al12mg17共晶温度437摄氏度，在共晶组织可以形成。这两个文件，虽然提出了不同的机制，形成共晶结构，表明，局部熔化，可以很容易地发生在搅拌摩擦焊或搅拌摩擦点焊铝合金镁合金。
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
佐藤等，被建议宪法熔析的可能性作为机制为共晶结构的形成在AA1050期间搅拌摩擦焊对AZ61。 另一方面， Gerlich和al.27举办了AA6111搅拌摩擦点焊对AZ91并且确定高峰温度在工具附近迅速地到达了a-Mg+Al12Mg17共晶温度437摄氏度，共晶微结构可能形成。 这二篇文章，虽然提出不同的机制为共晶结构的形成，表示，本机熔化可能容易地发生在Al合金期间搅拌摩擦焊或搅拌摩擦点焊对镁合金。
|
|
2013-05-23 12:26:38
佐藤等，suggested 到 AZ61 AA1050 搅拌摩擦焊共晶结构的形成机制作为宪法液化的可能性。另一方面，耶利克 et al.27 进行到 AZ91 AA6111 搅拌摩擦点焊，并确定该工具的附近的峰值温度迅速达到-镁 + Al12Mg17 共晶温度的 437摄氏度，共晶组织可以形成的。这两篇论文，尽管提出的共晶结构，形成不同的机制显示本地熔化可以轻松地期间发生搅拌摩擦焊或搅拌摩擦点焊 Al 合金镁合金。
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区