求翻译：The effect of anodic treatments on the corrosion resistance in Cl−-solutions and the structure of oxide layers on alloy AISI304 was investigated. Oxides were analysed using RBS, SEM and TEM. The highest pitting potential shifts (790 mV) are obtained by anodizing at high temperature (95 °C) within the passive range in a是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The effect of anodic treatments on the corrosion resistance in Cl−-solutions and the structure of oxide layers on alloy AISI304 was investigated. Oxides were analysed using RBS, SEM and TEM. The highest pitting potential shifts (790 mV) are obtained by anodizing at high temperature (95 °C) within the passive range in a
问题补充： |
|
2013-05-23 12:21:38
在Cl耐腐蚀的阳极处理效果 - 解决方案和AISI304合金的氧化层的结构进行了调查。氧化物使用RBS，SEM和TEM分析。最高点蚀潜在的变化（790 mV）以获得在酸浴的被动范围内，在高温（95℃）阳极氧化。使用这种方法有可能增长高达400纳米，是多孔纳米尖晶石构成的氧化物层。钼和铌纳入氧化层，但没有受益的耐腐蚀性能的改善，这是更大的氧化层的厚度和铬富集解释。
|
|
2013-05-23 12:23:18
阳极治疗的效果的抗腐蚀性能在CL——的解决办法和结构上的氧化层合金AISI304进行了调查。 氮氧化物是分析使用皇家苏格兰银行,教统局局长和TEM。 最高挖潜力转变(790mV)是由阳极氧化取得在高温度(95°C)范围内在的被动酸浴缸。 使用这种方法,有可能增加到400nm氧化物层,这是构成的多孔复合材料尖晶石。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
AISI304 合金的氧化层的结构和阳极处理对 Cl−-解决方案中耐腐蚀性能的影响进行了调查。使用 RBS 镜、 透射电镜分析氧化物。最高的点蚀电位变化 (790 mV） 通过高温 (
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区