求翻译：The long cyclic durability is a crucial problem for supercapacitors. The cycle stability of S0 and S3 was also evaluated at a current density of 1 A g−1for 5000 cycles, as shown in Figure 8. The Cs of S0 displays good cyclic ability with a slight decrease after 5000 cycles, which implies the MnO2 electrode exhibits goo是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The long cyclic durability is a crucial problem for supercapacitors. The cycle stability of S0 and S3 was also evaluated at a current density of 1 A g−1for 5000 cycles, as shown in Figure 8. The Cs of S0 displays good cyclic ability with a slight decrease after 5000 cycles, which implies the MnO2 electrode exhibits goo
问题补充： |
|
2013-05-23 12:21:38
长循环耐久性是超级电容器的关键问题。的S0和S3中的循环稳定性也评价为1 AG-1对于5000个周期的电流密度下，如示于图8。 S0显示器CS的良好的循环能力，有轻微的下降后，5000次，这意味着MnO2电极材料具有良好的电化学稳定性。 S3的cs的迅速下降在第2000次循环的开始，然后保持稳定值约75％的初始值。电容在长期循环的降低可能是由于PPD在电解系统中的不完全氧化还原反应
|
|
2013-05-23 12:23:18
长的循环耐久性是supercapacitors的一个关键的问题。如图8.所显示， S0和S3的周期稳定也被评估了在1个A g−1for 5000周期电流密度。S0电缆敷设船在5000个周期以后显示与轻微的减退的好循环能力，暗示MnO2电极展览好电化学稳定。S3电缆敷设船在2000th周期初迅速下降，然后保留稳定的价值大约75%原始价值。
|
|
2013-05-23 12:24:58
长的循环耐久性是一个关键的问题为supercapacitors。 S0和S3的周期稳定也被评估了在1 A g−1for 5000周期电流密度，如图8所显示。 S0 Cs在5000个周期以后显示好循环能力以轻微的减退，暗示MnO2电极展览好电化学稳定。 S3 Cs在2000th周期初迅速下降，然后保留稳定的价值大约75%原始价值。 电容减退在长期循环在电解系统也许归结于PPD的残缺不全的氧化还原的反应
|
|
2013-05-23 12:26:38
长循环耐久性是超级电容器的一个关键问题。S0 和 S3 的周期稳定还评价了，电流密度为 1 A g−1for 5000 周期，如图 8 所示。Cs S0 与略有下降的良好循环能力后，显示 5000 周期，这意味着 MnO2 电极陈列电化学稳定性好。Cs S3 跌的很快，2000 的周期的开始，然后不断稳定的价值约 75%的初始价值。长期骑自行车减少可能是电容的由于不完整的氧化还原反应的 PPD 电解系统中
|
|
2013-05-23 12:28:18
长循环的耐久性是对于超容器的一个至关重要的问题。S0 和 S3 的周期稳定性也在一电流密度 1 A g-1for 被评价 5000 个周期，如图 8 所示。S0 的 C 以少许的减少显示好循环的能力在 5000 个周期之后，意味着 MnO2 电极展览好电气化学的稳定性。S3 的 C 快速在第 2000 个周期的开始下跌，然后使一种稳定的价值大约 75% 最初价值中。长期的骑自行车中的电容的减少可能由于 PPD 在电解的系统中的不完整的 redox 反应
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区