求翻译：Cr23C6的析出引起Cr元素在晶界及其附近的贫化，介质中的Cl-在贫铬的晶界上富集而发生点蚀，并在拉应力作用下导致应力腐蚀开裂。是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Cr23C6的析出引起Cr元素在晶界及其附近的贫化，介质中的Cl-在贫铬的晶界上富集而发生点蚀，并在拉应力作用下导致应力腐蚀开裂。
问题补充： |
|
2013-05-23 12:21:38
cr23c6 precipitation caused by cl-cr elements in the grain boundary and near depleted medium enriched in chromium depletion of grain boundaries, the occurrence of pitting corrosion and stress corrosion cracking under tensile stress.
|
|
2013-05-23 12:23:18
The 6 23 Cr C Cr caused by elements in crystal clear and the nearby community of depleted, in the media - in Cl chromium-rich crystal sets, and pitting, and stress cause stress corrosion cracking.
|
|
2013-05-23 12:24:58
The Cr23C6 separation causes the Cr element in the crystal boundary and nearby impoverishment, in medium Cl- concentrates in the poor chromium crystal boundary has the pitting, and causes the stress corrosion dehiscence under the tensile stress function.
|
|
2013-05-23 12:26:38
Cr23C6 caused precipitation of Cr elements near the grain boundary and its depleted, Cl-poverty in the medium chrome pitting occurred on the grain boundary of enrichment, and under tensile stress cause stress corrosion cracking.
|
|
2013-05-23 12:28:18