求翻译：The ASTM slabs are to be molded for 6 minutes at 350oF + 5oF platen temperature as measured by a surface pyrometer. While molding the slabs, a minimum of 2,000 psi is to be maintained continuously and uniformly over the full slab surface for the vulcanization.是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The ASTM slabs are to be molded for 6 minutes at 350oF + 5oF platen temperature as measured by a surface pyrometer. While molding the slabs, a minimum of 2,000 psi is to be maintained continuously and uniformly over the full slab surface for the vulcanization.
问题补充： |
|
2013-05-23 12:21:38
ASTM砖被塑造为6分钟，在350of + 5of滚筒表面测温仪测量温度。而成型的砖，最低2000磅，是要保持连续和均匀在整个板坯表面的硫化。
|
|
2013-05-23 12:23:18
astmrest带可模制6分钟的+5的模板在350温度测量的表面高温计。 在注塑的rest带,在最小的是,要保持000磅 平方英寸不断和应均匀地分布在全带表面的硫化。
|
|
2013-05-23 12:24:58
ASTM平板将被铸造在6分钟在350oF + 5oF台板温度如由一支表面高温计测量。 当铸造平板时，最小限度于2,000 psi将连续和一致地被维护在充分的平板表面为硫化作用。
|
|
2013-05-23 12:26:38
ASTM 板都要在 350oF + 5oF 6 分钟模压屏式温度以表面测温仪衡量。同时成型板、 2000 （psi 的最低限度是硫化完整板坯表面上保持连续、 均匀。
|
|
2013-05-23 12:28:18
ASTM 厚平板是以 350oF + 5oF 压印盘温度 6 分钟来被塑造如通过一表面的 pyrometre 测量。当塑造厚平板时，至少 2,000 psi 是连续地和一贯地为了 vulcanization 在全部厚平板表面上被维持。
|