求翻译：According to the allowable stress values listed in the table, it is indicated that there is no any big difference between T911 and T91 steel while in the range 566-620℃, however, when the design metal temperature is 593℃, the P911 is higher than the P91 steel around 10%, so that on this design temperature, the wall thi是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
According to the allowable stress values listed in the table, it is indicated that there is no any big difference between T911 and T91 steel while in the range 566-620℃, however, when the design metal temperature is 593℃, the P911 is higher than the P91 steel around 10%, so that on this design temperature, the wall thi
问题补充： |
|
2013-05-23 12:21:38
根据表中所列的容许应力值，它表示t911和T91钢之间是没有任何大的差异，而在范围566-620℃，然而，当设计金属温度是593℃，P911是高比P91钢在10％左右，所以，在这个设计温度，头和主蒸汽管道的壁厚可以减少，如果使用P911钢。
|
|
2013-05-23 12:23:18
强调根据允许表中所列值,则表示,没有任何大的不同点t911和t91钢虽然 566-620° ℃范围中,但是,当设计金属温度为593°℃时,p911是高于p91钢10%左右,因此,在这设计温度,这堵墙的厚度的标题和主蒸汽管可以减少使用p911钢。
|
|
2013-05-23 12:24:58
根据在桌里列出的安全应力价值，它被表明没有T911和T91钢之间的所有大区别，当在范围566-620℃上时，然而，当设计金属温度是593℃时， P911 P91钢在10%附近高于，因此在这个设计温度，倒栽跳水的壁厚度和主要蒸汽管可以减少，如果用途P911钢。
|
|
2013-05-23 12:26:38
根据表中列出了允许应力值，它被表示有没有任何大 T911 和区别 T91 钢同时在范围 566-620℃，但是，当金属的温度是 593℃ 的设计、 P911 高于 P91 钢 10%左右，以便对这一设计温度，标题和主蒸汽管道的壁厚可减少如果使用 P911 钢。
|
|
2013-05-23 12:28:18
根据允许
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区