求翻译：To accomplish this study, a highly pure industrial mullite was used. Mullite with and without Y2O3 was pressed under a cold isostatic pressure of 200 MPa. Samples were sintered conventionally at 1400, 1450, 1500, 1550 and 1600 degrees C for 2 h and microwave-sintered for up to 40 min using a large range of power. The m是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
To accomplish this study, a highly pure industrial mullite was used. Mullite with and without Y2O3 was pressed under a cold isostatic pressure of 200 MPa. Samples were sintered conventionally at 1400, 1450, 1500, 1550 and 1600 degrees C for 2 h and microwave-sintered for up to 40 min using a large range of power. The m
问题补充： |
|
2013-05-23 12:21:38
完成这项研究中，使用高纯度工业莫来石。莫来石和无Y2O3压为200 MPa冷等静压下。样品常规为2小时，长达40分钟使用功率大范围微波烧结烧结在1400，1450，1500，1550和1600摄氏度。常规烧结样品的微波烧结样品的微观结构和物理性能进行了比较。结果表明，Y2O3改善传统和微波烧结过程中莫来石机构的致密化，但在短短几分钟内实现高densifications被当Y2O3与微波处理。
|
|
2013-05-23 12:23:18
为了完成这项研究,一个非常纯粹的产业莫来石的使用情况。 莫来石,并没有y2o3下按下了一个冷的压力机压力200mpa。 样本在常规烧结1400、1450、1500、1550和1600°℃,2h和微波烧结,可容纳40分钟用一个较大范围的电源。 在显微组织的物理属性和微波的烧结比较样本,这些样本的常规烧结。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
为了完成这项研究，用高纯度的工业莫来石。莫来石与无 Y2O3 按下冷等静压压力 200 兆帕斯卡。常规烧结 1400年、 1450年、 1500年、 1550年和 1600年度 C 2 h 样本并将其微波烧结达 40 分钟的使用范围大的权
|
|