求翻译：Similarly to polyimide-silica hybrid films,8 the modulus of the hybrid film increases in comparison with the original polyimide film. The electric properties of the polyimide were actually changed by introducing TiO2. Polyimide hybrid films containing 9.4% TiO2 had a dielectric constant of 3.6 and a dielectric dissipat是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Similarly to polyimide-silica hybrid films,8 the modulus of the hybrid film increases in comparison with the original polyimide film. The electric properties of the polyimide were actually changed by introducing TiO2. Polyimide hybrid films containing 9.4% TiO2 had a dielectric constant of 3.6 and a dielectric dissipat
问题补充： |
|
2013-05-23 12:21:38
类似聚酰亚胺 - 二氧化硅杂化膜，混合膜与原来的相比增加模聚酰亚胺薄膜。聚酰亚胺的电性能，实际上改变了通过引入二氧化钛。聚酰亚胺含有9.4％的TiO2复合薄膜介质常数3.6和一个0.003的介质损耗因数（3.0和原始聚酰亚胺薄膜0.001）相比。此外，复合薄膜不溶于NMP再次，即使经过长时间的加热。这表明，在复合薄膜中存在的某些无机相和聚合物基体之间的相互作用。
|
|
2013-05-23 12:23:18
同样,聚酰亚胺的硅混合films,8模数混合膜增加与原来相比聚酰亚胺薄膜。 聚酰亚胺的电属性的改变实际上介绍的tio2。 聚酰亚胺薄膜含有9.4%二氧化钛2混合了介电常数为3.6和一个介电损耗系数为0.003(与之相比,3.0和0.001的原始聚酰亚胺薄膜)。 此外,混合动力在nmp电影不能再次解散,即使在长时间加热。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
同样地，聚酰亚胺-二氧化硅杂化薄膜，混合膜的模量与原始的聚酰亚胺薄膜比较会增加的 8。聚酰亚胺的电气性能是通过引入 TiO2 实际更改的。聚酰亚胺薄膜含 9.4 %tio2 了 3.6 的介电常
|
|