求翻译：More detailed topology is shown in the 3-D image which shows that inorganic particles seem to be embedded in the film surface. The surface roughness of hybrid film was less than 30nm. The thermal stability of the hybrids was evaluated using TGA. The incorporation of TiO2 into polyimides did not greatly affect their the是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
More detailed topology is shown in the 3-D image which shows that inorganic particles seem to be embedded in the film surface. The surface roughness of hybrid film was less than 30nm. The thermal stability of the hybrids was evaluated using TGA. The incorporation of TiO2 into polyimides did not greatly affect their the
问题补充： |
|
2013-05-23 12:21:38
这表明无机粒子似乎被嵌入在薄膜表面的3-D图像显示更详细的拓扑。复合薄膜的表面粗糙度小于30nm的少。使用TGA杂交热稳定性进行了评估。没有纳入到聚酰亚胺二氧化钛大大影响其热性能。然而，热重分析表明，聚合物的分解温度，对应5％的重量损失，除了二氧化钛后降低。
|
|
2013-05-23 12:23:18
更多详细的拓扑结构所示是3-d图像,该图像显示,无机颗粒似乎嵌入式在胶片的表面上。 电影的表面粗糙度的混合型低于30nm。 杂交的热稳定性是评价使用tga。 将二氧化钛2polyimides没有极大地影响着其热属性。 但是,thermogravimetric分析表明,该聚合物分解温度,相当于5%的重量损失,此外还在跌幅的tio2。
|
|
2013-05-23 12:24:58
更加详细的拓扑结构在三维图象显示哪些
|
|
2013-05-23 12:26:38
在其中显示无机粒子似乎被内嵌在膜表面的三维图像显示更详细的拓扑。混合薄膜的表面粗糙度低于 30nm。热稳定性的混合动力车是使用 TGA 评估的。大大 TiO2 纳入聚酰亚胺并不会影响其热性能。然而，热重分析表示聚合物分解温度，对应的体重下降 5%，减少 TiO2 加入。
|
|