求翻译：The volume of polymerization mixture employed in the method of the instant invention is significantly smaller in other methods in which sufficient solvent or swelling agent is initially present to produce a gel structure immediately in the mold. For contact lenses having a diameter of 6 to 14 millimeters, the amount of是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The volume of polymerization mixture employed in the method of the instant invention is significantly smaller in other methods in which sufficient solvent or swelling agent is initially present to produce a gel structure immediately in the mold. For contact lenses having a diameter of 6 to 14 millimeters, the amount of
问题补充： |
|
2013-05-23 12:21:38
在即时发明的方法采用的聚合混合物的体积显着足够的溶剂或溶胀剂最初是立即在模具生产的凝胶结构的其他方法。接触有一个直径6毫米至14毫米的镜头，无溶剂单体混合物的数量实际上是如此之小，即使不发生气泡，如果聚合反应速率超过建议在前面的方法，保持温度，大幅增加在50摄氏度的混合物。或更高
|
|
2013-05-23 12:23:18
采用的卷的聚合混合物的方法发明的小了很多的即时的溶剂或其他方法,使充分膨胀剂是目前生产的凝胶结构最初立即在模具上。
|
|
2013-05-23 12:24:58
在瞬时发明方法使用的聚化混合物的容量是显着小在充足的溶剂或泡胀剂最初是存在导致一%
|
|
2013-05-23 12:26:38
受雇于即时发明的方法的聚合混合料的体积是显著较少的其他方法的足够溶剂或膨胀剂是最初目前生产模具中立即凝胶结构。隐形眼镜有一个直径为 6 到 14 毫米的无溶剂单体混合料量是竟然这么小的气泡不会发生即使聚合速度大幅增加以上较早的方法中推荐的保持在 50 度 C 混合物的温度。或更高
|
|