求翻译：Subsequently, a desired amount of pretreated AC and Mn-Zn ferrite particles were dispersed into ethanol in an ultrasonic bath for 30 min. Then 10mL CaO solution (0.002 mol L−1) was added into the above mixture with vigorously stirring for 3min. A hydrochloric acid solution was used to adjust the pH value of the solutio是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Subsequently, a desired amount of pretreated AC and Mn-Zn ferrite particles were dispersed into ethanol in an ultrasonic bath for 30 min. Then 10mL CaO solution (0.002 mol L−1) was added into the above mixture with vigorously stirring for 3min. A hydrochloric acid solution was used to adjust the pH value of the solutio
问题补充： |
|
2013-05-23 12:21:38
随后，所需数量的预处理的交流和Mn-Zn铁氧体颗粒分散成乙醇在超声波浴30分钟。 10毫升曹解决方案（0.002摩尔L-1），然后加入上述混合物大力搅拌3分钟。用盐酸溶液调整pH值2.2的解决方案。搅拌30分钟后，磁铁分离固体样品，用蒸馏水冲洗，然后在50℃干燥。
|
|
2013-05-23 12:23:18
后来,所希望的金额的预处理交流和mn-zn铁氧体磁微粒的分散到乙醇在超声波浴30分钟。然后10ml曹解决方案(0.002moll-1)和空气的混合,添加到上述用力搅拌3分钟。 解决方案是使用一个盐酸液的ph值调整到2.2。 搅动后的30分钟,在坚实的样本被分隔的磁铁,用清水冲洗蒸馏水,然后在50°℃干燥。
|
|
2013-05-23 12:24:58
随后，期望相当数量被预处理的AC和Mn锌纯铁微粒在超音波浴被分散了入对氨基苯甲酸二30 min。 然后10mL CaO解答(0.002 mol L−1)增加了入上述混合物以苍劲搅动为3min。 一种盐酸解答用于调整解答的PH值到2.2。 在搅动在30分钟以后，坚实样品由磁铁分离，用蒸馏水漂洗了然后被烘干了在50℃。
|
|
2013-05-23 12:26:38
随后，期望的数量的预处理的交流和锰锌铁氧体粒子分散成 30 分钟超声浴中乙醇。然后 10 毫升曹解决方案 （0.002 mol L−1） 都被添加到上述混合物大力搅拌 3 分钟。盐酸溶液中被用来调整到 2.2 溶液的 pH 值。后 30 分钟的搅拌，固体样品被分隔磁铁、 用蒸馏水冲洗和再擦干 50 ℃。
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区