求翻译：Stress corrosion cracking mechanisms have been investigated extensively. It has been found that acoustic emission signals are produced from both brittle crack propagation and plastic blunting of crack tips. In the case of transgranular crack propagation, the acoustic emission signal production is mainly a mechanical ef是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Stress corrosion cracking mechanisms have been investigated extensively. It has been found that acoustic emission signals are produced from both brittle crack propagation and plastic blunting of crack tips. In the case of transgranular crack propagation, the acoustic emission signal production is mainly a mechanical ef
问题补充： |
|
2013-05-23 12:21:38
应力腐蚀开裂机制已被广泛研究。它已被发现，声发射信号的脆性裂纹扩展裂纹尖端钝化和塑料的生产。穿晶裂纹扩展的情况下，声发射信号的生产主要是机械的作用，导致裂纹扩展的连续步骤。声发射信号也被发现，并明确确定的晶间应力腐蚀裂纹扩展 - 例如，在统一的编码系统32 n06600镍铬合金。这种机制可能不是纯粹
|
|
2013-05-23 12:23:18
他们已经调查了应力腐蚀开裂机制广泛。 人们已经发现,噪音排放信号将从这两个易碎的破解破解传播和塑料用钝之后可以提示。 transgranular传播破解的案件中的,噪音排放信号,主要是一个生产机械造成不连续步骤在破解传播。
|
|
2013-05-23 12:24:58
应力腐蚀裂化机制广泛地被调查了。 它被发现声发射信号由易碎的裂纹扩展和塑料钝裂缝技巧导致。 在transgranular裂纹扩展情况下，声发射信号生产是主要一个机械作用起因于不连续的步在裂纹扩展。 Acoustic emission signals have also been detected and clearly identified from intergranular stress corrosion crack propagation — for instance, in Unified Numbering System 32 N06600 nickel chromium allo
|
|
2013-05-23 12:26:38
广泛进行调查应力腐蚀开裂机制。已找到声发射信号产生脆性裂纹扩展和裂纹尖端塑性钝化。在晶裂纹扩展、 声发射信号生产是主要力学效应产生的裂纹扩展过程中不连续的步骤。声发射信号也已检测到从已清楚确定的晶间应力腐蚀裂纹扩展 — — 例如，在统一编号系统 32 N06600 镍铬合金。这一机制可能不是纯粹
|
|
2013-05-23 12:28:18
使机制爆裂的压力腐蚀状态广泛被调查了。被找到了那声学排放发信号从两个都被生产脆弱高明的传播和塑料可卡因的秘诀的将弄钝。在跨颗粒高明的传播的情况下，声学排放信号生产主要是因在高明的传播中的不连续的步骤而产生的一种机械效果。声学排放发信号也发现和清楚地从互相颗粒的压力腐蚀状态裂缝传播确定 - 例如，在成一体的计数系统中 32 N06600 镍铬合金。这种机制不愿纯粹是
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区