求翻译：总和分析高炉炉衬的破损机理发现，高温时炉衬破损的根本条件，其次是渣铁液、碱金属的侵蚀，机械冲刷、渗漏、涨缩开裂、磨损等的动力作用也不可忽视，但就主次来说，应着重从传热学来分析，其次也要从化学侵蚀、动力学来研究，才能得到合理的炉衬结构。是什么意思？

Sum of the analysis of blast furnace lining damage mechanism found lining damaged at high temperatures the fundamental condition, followed by the residue of molten iron, alkali metal erosion, mechanical erosion, leakage, up to shrinkage cracking, abrasion, such as dynamic action should not be ignore

Total blast furnace lining and analysis of the broken-down, found at high temperature furnace lining, damaged the underlying conditions, followed by Standard Chartered rail, the alkalis, mechanical scouring erosion, leakage, cracking, up scale the dynamic role of wear cannot be ignored, but also on

The sum total analysis blast-furnace lining breakage mechanism discovered, when high temperature the furnace lining breakage basic condition, next is the dregs iron liquor, the alkaline metal corrosion, the machinery washout, the leakage, rises shrinks the dehiscence, the attrition and so on the dyn

Sum analysis BF lining of damaged mechanism found, high temperature Shi lining damaged of fundamental conditions, second is slag iron liquid, and alkali metal of erosion, machinery scour, and leakage, and rose shrink crack, and wear, of power role also not ignored, but on primary and secondary,, sho

正在翻译，请等待...