求翻译：As could be confirmed in the previous section, the water sensitivity test results of both HMA and WMA mixtures are similar (respectively, 68.3% and 62.5% of retained strength after a conditioning period in water). However, in order to confirm if the WMA mixture would perform as well as the HMA mixture, a more comprehen是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
As could be confirmed in the previous section, the water sensitivity test results of both HMA and WMA mixtures are similar (respectively, 68.3% and 62.5% of retained strength after a conditioning period in water). However, in order to confirm if the WMA mixture would perform as well as the HMA mixture, a more comprehen
问题补充： |
|
2013-05-23 12:21:38
在上一节中可以证实，HMA和WMA混合物的水敏感性测试结果相似（分别为68.3％和保留实力的62.5％后，在水的调理期）。然而，为了确认，如果WMA混合物会执行以及HMA混合，更全面的测试系列进行，其中包括车辙性，刚度模量和疲劳开裂性测试。在这项研究中所取得的成果是在下面的小节。
|
|
2013-05-23 12:23:18
这一点可以确认,上一节中,水的这两个敏感度测试结果hma和wma混合物相似(分别为68.3%和62.5%的保留实力的空调期间后在水面)。 然而,为了确认如果wma混合物将执行以及hma混合,一个更全面的一系列测试,其中包括墨守成规,拥有优异的刚度系数和抗疲劳开裂试验。
|
|
2013-05-23 12:24:58
和在前面的部分能被证实， HMA和WMA混合物的水敏感性试验结果是相似的(分别， 68.3%和62.5%保留的力量在一个适应的期间以后在水中)。 然而，为了证实WMA混合物是否将执行以及HMA混合物，测试更加全面的系列被执行了，包括车轮痕迹抵抗、僵硬模数和疲劳裂化的电阻试验。 在这项研究中得到的结果在以下分部被提出。
|
|
2013-05-23 12:26:38
上一节中确认，沥青混合料和 WMA 的混合料水敏感性测试结果是类似 （分别 68.3%和 62.5%的残留强度调节期后水中）。然而，为了确认是否 WMA 混合物会执行，以及沥青路面混合料，进行更全面的一系列测试，其中包括抗车辙能力、 刚度模量和疲劳裂纹扩展电阻测试。在这项研究中获得结果下面的小节中。
|
|
2013-05-23 12:28:18
如可以在以前的部分，高端内存区和 WMA 混合物的水敏感实验结果中被确认是类似的 ( 分别地， 68.3% 和 62.5% 被保留的力量在水中的一段使人适应时期之后 )。然而，以确认如果 WMA 混合会像高端内存区混合一样好地执行，一次更全面系列的测试被进行，这包括在抵抗形成车辙，僵硬模数和使使人爆裂抵抗疲劳检查。结果在这项研究中获得在以下子章节中被赠送。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区