求翻译：Stress-rupture results are summarized in Table 7. The 2000° and 2200°F data are charted in Figs. 26 and 27, respectively. There was sufficient scatter in the time-to- rupture results to prevent determination of fine relation¬ships. However, the general conclusions are that for both test temperatures and sheet thickness是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Stress-rupture results are summarized in Table 7. The 2000° and 2200°F data are charted in Figs. 26 and 27, respectively. There was sufficient scatter in the time-to- rupture results to prevent determination of fine relation¬ships. However, the general conclusions are that for both test temperatures and sheet thickness
问题补充： |
|
2013-05-23 12:21:38
应力破裂的结果列于表7。 2000°和2200°F的数据绘制在图。分别为26和27。有足够的时间到破裂的结果分散，以防止良好的关系¬船舶的决心。但是，一般的结论是，试验温度和板材厚度，没有的具体DETE¬应力断裂性能rioration是显而易见的。作为外套¬ING成分扩散到基地的TD-镍，伸长率
|
|
2013-05-23 12:23:18
应力破裂结果总结于表7。 2000年和2200°°f数据进行制表的无花果。 26日和27日,分别。 有足够的时间散在的结果,防止破裂的决心就罚款船舶事宜。 然而,一般性结论是,对于这两个试验温度和厚度,没有具体的dete¬rioration应力破裂属性是不言自明的。 jointing选民分散的涂层的基座td-镍、延伸率
|
|
2013-05-23 12:24:58
注重破裂结果在表7总结。 2000°和2200°F数据在Figs.绘制。 26和27，分
|
|
2013-05-23 12:26:38
表 7 中概述了应力破裂的结果。用 2000 ° 和 2200 ° F 数据图表无花果 26 和 27，分别。防止细 relation¬ships 测定时间-破裂结果中有足够的散点图。然而，一般的结论是这对于测试温度和板材厚度，没有具体的应力破裂属性 dete¬rioration 是显而易见的。作为 coat¬ing 成分渗入基地 TD-镍、 伸长率
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区