求翻译：The surface morphology and particle size of the virginal and magnesium-doped lithium iron phosphate samples are shown in Figs. 3 and 4 . SEM micrographs in Fig. 3 show that the product particles are spherical, their diameter is about 0.1–0.5 μm, and TEM image in Fig.4 shows both virginal and doped LiFePO4 have particle是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The surface morphology and particle size of the virginal and magnesium-doped lithium iron phosphate samples are shown in Figs. 3 and 4 . SEM micrographs in Fig. 3 show that the product particles are spherical, their diameter is about 0.1–0.5 μm, and TEM image in Fig.4 shows both virginal and doped LiFePO4 have particle
问题补充： |
|
2013-05-23 12:21:38
处女和镁掺杂磷酸铁锂样品的表面形貌和粒子大小都显示在无花果。 3和4。 SEM照片图。 3表明，产品颗粒呈球形，直径约0.1-0.5微米，和TEM图像处女和掺杂的LiFePO4图显示大约有50-100纳米颗粒大小，颗粒松散的结块。小颗粒，松散agglomerat版结构允许电解液容易渗透，并提供了一个短的锂离子的活性物质的扩散途径。
|
|
2013-05-23 12:23:18
表面形态和大小的颗粒的多么纯洁的和镁的麻痹锂铁磷酸盐样品显示在无花果。 3和4。 教统局局长答称,图显微照片。 图3显示,产品颗粒球形,直径约为0.1-0.5μm,tem图像图4显示了两个多么纯洁,麻痹了用于lifepo4颗粒尺寸约50-100纳米,这些颗粒会集中于某些松散。
|
|
2013-05-23 12:24:58
十六，七世纪小型有键乐器的表面形态学和微粒大小和镁被掺杂的锂铁磷酸盐样品在Figs.显示。 3和4。 SEM微写器在。 3展示产品微粒是球状的，他们的直径是大约0.1-0.5 μm，并且TEM图象在展示处女和被掺杂的LiFePO4有颗粒大小在50-100毫微米附近，并且微粒宽松地成块。 小颗粒和agglomerat编辑结构在放射性材料宽松地允许电解质的容易的渗透并且为锂离子扩散提供一条短的路。
|
|
2013-05-23 12:26:38
正在翻译，请等待...
|
|
2013-05-23 12:28:18
童贞和镁用药物刺激的锂铁磷酸盐的表面的构词学和微粒大小采样在无花果被显示。3 和 4。在无花果中的 SEM 显微图。3 显示产品微粒是球面的，他们的直径关于 0.1-0.5？m，在 Fig.4 的 TEM 图像显示两个都童贞和用药物刺激 LiFePO4 有微粒在 50-100 nm 附近的大小，以及微粒被松地成团。小微粒和松地 agglomerat ed 结构允许电解液的容易的渗透和提供一条短的路用于在活动材料中的锂离子的散布。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区