求翻译：Mesoporous TiO2 was prepared from Potassium titanate (K2Ti2O5) according to our previous work.1 In short, K2Ti2O5 was ion exchanged with HCl aqueous solution (0.1 M) to be hydrated titanate (H2Ti2O5). Then, the calcinations of H2Ti2O5 were performed in a muffle oven at 550 oC to obtain mesoporous TiO2. The structural d是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Mesoporous TiO2 was prepared from Potassium titanate (K2Ti2O5) according to our previous work.1 In short, K2Ti2O5 was ion exchanged with HCl aqueous solution (0.1 M) to be hydrated titanate (H2Ti2O5). Then, the calcinations of H2Ti2O5 were performed in a muffle oven at 550 oC to obtain mesoporous TiO2. The structural d
问题补充： |
|
2013-05-23 12:21:38
介孔TiO2从酸钾（k2ti2o5）准备根据以往我们在短期work.1中，k2ti2o5是离子交换盐酸溶液（0.1米）水合钛酸（h2ti2o5）。然后，在550℃煅烧h2ti2o5获得介孔TiO2，在马弗炉。介孔TiO2的结构数据表明，在表1
|
|
2013-05-23 12:23:18
二氧化钛吸收的钾mesoporous编写了钛酸铝2(k2ti2o5),根据我们以前工作1简而言之,k2ti2o5是离子交换hcl水溶液(0.1m)水合钛酸钡(h2ti2o5)。 然后,calcinationsh2ti2o5是一种在抑制烤箱在550ocmesoporoustio2获得。 mesoporous二氧化钛的结构性数据的显示在表12。
|
|
2013-05-23 12:24:58
Mesoporous TiO2从钾钛酸盐(K2Ti2O5)准备了简而言之根据我们的早先work.1， K2Ti2O5是离子交换与HCl水溶液(0.1 M)是水合的钛酸盐(H2Ti2O5)。 然后， H2Ti2O5的锻烧在一个裹住烤箱进行在550 oC获得mesoporous TiO2。 mesoporous TiO2结构数据在表1显示了
|
|
2013-05-23 12:26:38
介孔 TiO2 准备从钾钛酸 (K2Ti2O5) 据以我们以前的 work.1 简而言之，K2Ti2O5 是离子交换与盐酸溶液是水合钛酸 (H2Ti2O5) (0.1 M)。然后，煅烧特性的 H2Ti2O5 是在 550 业主立案法团获得介孔 TiO2 马弗炉中进行的。TiO2 介孔结构的数据都显示在表 1 中
|
|
2013-05-23 12:28:18
Mesoporous TiO2 从钾 titanate 准备 ( K2Ti2O5 ) 根据我们的以前的 work.1 简而言之， K2Ti2O5 是有 HCl 被交换的离子水的解决方案 (0.1 米 ) 被与水化合 titanate( H2Ti2O5 )。然后， H2Ti2O5 的煅烧在 550 oC 处
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区