求翻译：The FESEM images of ZnO nanostructures prepared from the different zinc hydroxide precursors are presented in Fig. 3. The ZnO nanoparticles were achieved by the post-annealing treatment of amorphous zinc hydroxides mi-croparticles, as shown in Fig. 3(a). The average diameter of ZnO nanoparticles was about 50 nm. The 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The FESEM images of ZnO nanostructures prepared from the different zinc hydroxide precursors are presented in Fig. 3. The ZnO nanoparticles were achieved by the post-annealing treatment of amorphous zinc hydroxides mi-croparticles, as shown in Fig. 3(a). The average diameter of ZnO nanoparticles was about 50 nm. The
问题补充： |
|
2013-05-23 12:21:38
准备从不同的氢氧化锌的前体的氧化锌纳米结构的FESEM影像图。 3。纳米ZnO实现由无定形锌氢氧化物MI - croparticles如图所示，后退火处理。 3（A）。 ZnO纳米粒子的平均直径约为50 nm。取得了多孔的氧化锌纳米片结晶锌（OH）（NO3）（H2O）纳米带后退火处理，如下所示
|
|
2013-05-23 12:23:18
图像的fesem氧化锌的纳米构造合编写的前体不同锌氢氧化列在图。 3. 颗粒的氧化锌取得的后处理退火的非晶锌溶液美croparticles,见图2)。 3(a)。 平均的氧化锌颗粒的直径约50nm。 漏洞百出的氧化锌nanosheets取得的后退火治疗的结晶ZN(OH)(没有.3)(H2O)nanobelts,见
|
|
2013-05-23 12:24:58
ZnO nanostructures的FESEM图象从不同的锌氢氧化前体准备的被提出在。 3. ZnO nanoparticles由无定形的锌氢氧化微粒的岗位焖火治疗达到，如所显示。 3 (a)。 ZnO nanoparticles平均直径约为50毫微米。 多孔ZnO nanoshe
|
|
2013-05-23 12:26:38
氧化锌纳米材料准备从不同锌氢氧化前体的 FESEM 图像以图。3.氧化锌纳米粒子被取得的氢氧化物 mi croparticles 非晶锌，后处理治疗，如图中所示。3 (a)。氧化锌纳米粒子的平均直径为约 50 nm。多孔氧化锌纳米被取得的纳米带 Zn(OH)(NO3)(H2O) 结晶，后处理治疗，如中所示
|
|