求翻译：Preparation of zinc hydroxide precursors: The chemical bath deposition was adopted for the synthesis of zinc hydrox-ide precursors. The chemical solution was composed of zinc nitrate hexahydrate (Zn(NO3)2•6H2O) (0.2 ml−1), urea (0.2 ml−1). The pH value and the temperature of the solu-tion were maintained at 7.8 and 60°是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Preparation of zinc hydroxide precursors: The chemical bath deposition was adopted for the synthesis of zinc hydrox-ide precursors. The chemical solution was composed of zinc nitrate hexahydrate (Zn(NO3)2•6H2O) (0.2 ml−1), urea (0.2 ml−1). The pH value and the temperature of the solu-tion were maintained at 7.8 and 60°
问题补充： |
|
2013-05-23 12:21:38
氢氧化锌的前体的制备：采用锌羟基- IDE前体的合成化学浴沉积。六水合硝酸锌（以Zn（NO3）2•6H2O）（0.2 ML - 1），尿素（0.2 ML - 1）的化学溶液组成。溶液中的pH值和温度均保持在7.8和60℃，分别。 20小时和60小时的沉积，两种类型的氢氧化锌沉淀后，即无定形锌氢氧化物micropar颗粒结晶锌（OH）（NO3）（H2O）纳米带，离心收集，并用去离子水多次清除。为了准备可溶性的氢氧化锌品种，后得到沉淀物沉积60 h分别到氢氧化钠溶液（0.5 ML - 1）溶解，溶液搅拌30分钟，以形成水溶性锌（OH）24 - 物种。
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
锌氢氧化前体的准备： 化工浴证言为锌氢氧化前体综合被采取了。 化工解答由%E
|
|
2013-05-23 12:26:38
正在翻译，请等待...
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区