求翻译：The corrosion behavior of 316L stainless steel (316L) and bulk amorphous Zr75Ti25 (AB) alloy was studied using electrochemical noise (EN) in simulated polymer electrolyte membrane fuel cell (PEMFC) conditions at 25 and 80 °C. At open circuit potential, under H2 environment, AB exhibited a higher corrosion-resistance th是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The corrosion behavior of 316L stainless steel (316L) and bulk amorphous Zr75Ti25 (AB) alloy was studied using electrochemical noise (EN) in simulated polymer electrolyte membrane fuel cell (PEMFC) conditions at 25 and 80 °C. At open circuit potential, under H2 environment, AB exhibited a higher corrosion-resistance th
问题补充： |
|
2013-05-23 12:21:38
316L不锈钢（316L）和大块非晶Zr75Ti25（AB）合金的腐蚀行为进行了研究使用模拟聚合物电解质膜燃料电池（PEMFC）的条件，在25和80 ° C的电化学噪声（EN）在开路电位，H2的环境下，AB公司展出了超过316较高的耐腐蚀，相反氧气环境下观察。施加阴极电位，H2质子交换膜燃料电池阳极模拟环境下316L减少机制，在80 ° C给所有其他条件的最重要的EN信号。施加阳极电位，O2阴极模拟环境下，处于被动状态为316L，而严重的局部腐蚀为AB明显，在80 ° C。它是结束这项工作的腐蚀数据，一个质子交换膜燃料电池的阳极环境中，AB合金，可能是一个比双极板316L更好的人选。与此相反的
|
|
2013-05-23 12:23:18
行为的腐蚀的不锈钢316L(316L)和散装非晶ZR75Ti25(ab)合金是研究用电化学噪音(EN)在模拟高分子电解膜燃料电池(pemfc)条件在25和80°C 在打开电路
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区