求翻译：A commercial 304 stainless steel Fe-18.5Cr-9.6Ni was passivated in 0.1 M H2SO4 solution at +750 mV(SHE) for 1 h at room temperature. The alloying effect of nickel was discussed in comparison with Fe-17Cr and Fe-15Cr-4Mo steels. The selectivity factor S was defined and used to characterize the dissolution behaviour of i是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
A commercial 304 stainless steel Fe-18.5Cr-9.6Ni was passivated in 0.1 M H2SO4 solution at +750 mV(SHE) for 1 h at room temperature. The alloying effect of nickel was discussed in comparison with Fe-17Cr and Fe-15Cr-4Mo steels. The selectivity factor S was defined and used to characterize the dissolution behaviour of i
问题补充： |
|
2013-05-23 12:21:38
一个商业的304不锈钢的Fe - 18.5Cr - 9.6Ni在750毫伏在室温下1小时（她）在0.1 M H2SO4溶液中钝化。与Fe - 17Cr和15Cr - 4Mo钢铁相比，镍合金的作用进行了讨论。选择性因子S被定义用来描述各个组件的溶出行为。解决方案电感耦合等离子体质谱（ICP - MS）分析了确凿证据的选择性溶解镍和铬钝化液中的损耗。随后的钝化膜表面的XPS分析表明氧化镍钝化膜，这是选择性溶解在溶液中的镍占的情况下。铬钝化膜的富集特点富集系数。 ICP - MS的结果计算出来的钝化膜的厚度为0.82纳米。椭偏文学价值的和谐。
|
|
2013-05-23 12:23:18
一个商业304不锈钢 Fe -18.5 CR -9.6倪 是钝化在0.1m H2SO4解决方案在+750MV(她)为1H在室温下。 镍合金的影响的讨论是在比较与FE-17CR和FE-15CR-4帽钢。 选择性的因素s是界定和使用的特点,解散行为个别组件。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
商业 304 不锈钢铁-18.5Cr-9.6Ni +750 mV(SHE) 1 h 在室温为 0.1 M 硫酸致死性溶液中钝化。镍
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区