求翻译：Hydrogen effects on the fracture stress of passive film formed on 316L stainless steel were studied by nanoindentation. Hydrogen accumulated primarily on the sample surface and in the passive film. Displacement excursion related to film fracture appeared in load-controlled load–displacement curves when electrochemicall是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Hydrogen effects on the fracture stress of passive film formed on 316L stainless steel were studied by nanoindentation. Hydrogen accumulated primarily on the sample surface and in the passive film. Displacement excursion related to film fracture appeared in load-controlled load–displacement curves when electrochemicall
问题补充： |
|
2013-05-23 12:21:38
由压痕氢316L不锈钢上形成的钝化膜的断裂应力的影响进行了研究。氢积累主要在样品表面的钝化膜。与电影骨折有关的位移偏移出现在负荷控制的载荷 - 位移曲线，电化学抛光和阳极钝化的样品被缩进。游览消失后的钝化膜电化学或由nanowear被删除。关键负载，旅行的深度和长度随氢浓度较高，随着杨氏模量和断裂应力的钝化膜。
|
|
2013-05-23 12:23:18
氢的骨折强调影响的被动电影形成的关于316L不锈钢nanoindentation研究了。 氢累积主要的样本表面和在被动电影。 游览流离失所有关电影骨折出现在负载控制负载流离失所时曲线钢板采用镀锡抛光和anodically钝化样本呈锯齿状。 之后失踪的游览的消能电影被钢板采用镀锡或由nanowear。
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
316L 不锈钢钝化膜的断裂应力对氢影响了纳米压痕法研究。氢积累主要对样品表面钝化膜中。有关电影骨折的位移漂移出现在负载控制 load–displacement 曲线时电化学抛光和阳极钝化的样本缩进。这次远足消失后钝化膜中移除了电
|
|