求翻译：This observation indicates that the interfacial force increases because of the π -π reaction between phenyl group on P-PN particle surface and polystyrene block (and phthaloyl groups in polyester block) in the matrix, and this hinders the segmental motion of the polyester and polystyrene blocks of the matrix. On this b是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
This observation indicates that the interfacial force increases because of the π -π reaction between phenyl group on P-PN particle surface and polystyrene block (and phthaloyl groups in polyester block) in the matrix, and this hinders the segmental motion of the polyester and polystyrene blocks of the matrix. On this b
问题补充： |
|
2013-05-23 12:21:38
这个观察结果显示，界面的力量，因为P-PN颗粒表面和聚苯乙烯块矩阵（邻苯二甲团体和聚酯块）苯基组之间的π-π反应增加，这阻碍了运动节段的聚酯，聚苯乙烯矩阵块。在此基础上，最大的π - π的界面力发生在CA PN内容。 10％。的储能模量的变化，很显然，除了P-PN产生混合动力车的储能模量明显效果。 PN的内容的增加将增加储能模量的钙含量与Pn点。如上所述，10％。然而，除了这一点，无机相就可以开始形成结块，这可能会增加脆性模数降低的程度
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
这观察表明界面的力量增加由于π - π反应在苯基在P-PN微粒表面和多苯乙烯块(和phthaloyl小组之间在聚酯块)在矩阵和这妨害矩阵的聚酯和多苯乙烯块的分装式行动。 根据这个依据，最大π - π界面的力量发生在PN内容约。 10 wt %。 至于存贮模数的变动，它是确切P-PN的加法提升明显的作用对杂种的存贮模数。 在PN的内容的增量将增加存贮模数由点决定与PN内容约。 10 wt %如上所述。 在这点之外，然而，无机阶段可能开始形成块集岩，可能增加易碎性在降低上模数的程度
|
|
2013-05-23 12:26:38
这一观察指示界面力增加 π-π 与反应 P PN 颗粒表面和聚苯乙烯块苯基组 （甲酰组聚酯块中的） 在矩阵，因为这阻碍了聚酯和矩阵的聚苯乙烯块运动节段。基于此，最大的 π-π 界面力发生在 PN 内容的 ca。 10 wt %。以存储弹性模量的改变，很明显的 P PN 添加引起效果明显的混合动力车的储能模量。Pn 结的内容的增加将会增加达 PN 内容的 ca。 10 点存储模量上文所述的 wt %。除了这一点，然而，无机相可以开始还可能增加的范围内降低模数的脆性的形式凝聚
|
|