求翻译：First, the geopolymer paste according to the designed ratio (Na2O:Al2O3=0.8, SiO2:Al2O3=2.88-3.12, H2O:Na2O=14-20) was prepared by mechanically mixing the metakaolin, modified sodium silicate solutions and deionized water for 10 min at 2000 rpm. Place the geopolymer paste in a self-made vacuum defoaming device, run at 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
First, the geopolymer paste according to the designed ratio (Na2O:Al2O3=0.8, SiO2:Al2O3=2.88-3.12, H2O:Na2O=14-20) was prepared by mechanically mixing the metakaolin, modified sodium silicate solutions and deionized water for 10 min at 2000 rpm. Place the geopolymer paste in a self-made vacuum defoaming device, run at
问题补充： |
|
2013-05-23 12:21:38
首先，地质聚合物糊按设计比（ Na2O的：氧化铝= 0.8的SiO 2 ：氧化铝= ,2.88-3 .12 H 2 O ：Na2O的= 14-20 ）通过机械混合的偏高岭土，改性的硅酸钠溶液和去离子水和10
|
|
2013-05-23 12:23:18
首先，根据被设计的比率(Na2O的geopolymer浆糊：Al2O3=0.8， SiO2 ：Al2O3=2.88-3.12， H2O ：Na2O=14-20)通过机械混和metakaolin、修改过的硅酸钠解答和被去离子的水准备在10在2000个转每分钟的分钟。安置geopolymer浆糊在一个自制真空消去设备，跑在真空程度0.1 MPa，直到没有泡影。
|
|
2013-05-23 12:24:58
正在翻译，请等待...
|
|
2013-05-23 12:26:38
第一，地质聚合物材料粘贴按设计比例 （Na2O:Al2O3 = 0.8，SiO2:Al2O3 = 2.88-3.12，H2O:Na2O = 14-20） 制得了机械混合偏高岭土、 改性硅酸钠溶液和去离子水 10 分钟在 2000 转 分。将无机矿物聚合物材料粘贴放在自制的真空消泡装置，在真空度 0.1 MPa 的运行，直到没有泡沫。由此产生的泥浆被放在塑料模具中，固化在加热器在 60 ° C 的 24 h 然后其按压它得到无机膜 [12-13]。
|
|