求翻译：Optical examination of the ultralight microlattices during deformation suggests that deformation initiates by local buckling at the nodes(Fig. 2, E and F). A closer inspection of the microlattices by scanning electron microscopy (SEM) shows that cracks and wrinkles are introduced primarily at the nodes during compressi是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Optical examination of the ultralight microlattices during deformation suggests that deformation initiates by local buckling at the nodes(Fig. 2, E and F). A closer inspection of the microlattices by scanning electron microscopy (SEM) shows that cracks and wrinkles are introduced primarily at the nodes during compressi
问题补充： |
|
2013-05-23 12:21:38
超轻microlattices变形过程中的光学检验表明，变形开始通过在节点局部屈曲（图2 ， E和F） 。
|
|
2013-05-23 12:23:18
超轻型的microlattices的光学考试在变形时通过地方折建议变形发起在结(图2， E和F)。microlattices的结束检查通过扫描电子显微镜术(SEM)表示在压缩(图2， G和H)期间，镇压和皱痕被介绍主要在结。
|
|
2013-05-23 12:24:58
ultralight microlattices的光学考试在变形期间通过地方折建议变形发起在结(。 2， E和F)。 microlattices的结束检查通过扫描电子显微镜术 (SEM) 表示，镇压和皱痕被介绍主要在结在压缩期间 (。 2， G和H)。 这损伤负责对在第一个压缩周期以后被观察的1到2%残余的张力，并且对下落在出产量和模数在随后压缩周期期间。 一旦稳定的“安心崩裂”形式在结，疏松microlattice材料在坚实镍亚磷材料不可能通过广泛的自转接受大有效的压缩张力关于残余结韧带，但以微不足道的张力，因而要求进一步破裂或塑料变形。 这物产导致在Figs.显示的反演性压缩行为。 2和3
|
|
2013-05-23 12:26:38
超轻型飞机 microlattices 变形过程中的光学检查表明变形通过局部屈曲 （图 2、 E 和 F） 的节点上启动。通过扫描电子显微镜 (SEM) microlattices 仔细检查显示裂缝和皱纹主要分别在引入节点压缩 (图 2、 G 和 H) 期间。这种损害负责观察后的第一次压缩周期，以及对于屈服强度和模量下降在随后压缩循环过程中的 1 到 2%残余应变。一次稳定的"救济裂缝"的形式在节点，散装 microlattice 材料可以接受通过广泛轮换有关节点韧带残，但可以忽略不计应变中的固体的镍磷物质，因而无需进一步断裂或塑性变形大有效压缩应变。此属性在图 2 和 3 所示的可逆压缩行为
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区