求翻译：0.5wt% of Au was supported on K-OMS-2 and Ce–K-OMS-2 by double incipient wetness impregnation (DIWI). DIWI consists of a first impregnation step using a solution of HAuCl4 (using sonication), followed by addition of an aqueous solution of Na2CO3 (1 M), under constant ultrasonic stirring. The resulting solid was washed 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
0.5wt% of Au was supported on K-OMS-2 and Ce–K-OMS-2 by double incipient wetness impregnation (DIWI). DIWI consists of a first impregnation step using a solution of HAuCl4 (using sonication), followed by addition of an aqueous solution of Na2CO3 (1 M), under constant ultrasonic stirring. The resulting solid was washed
问题补充： |
|
2013-05-23 12:21:38
正在翻译，请等待...
|
|
2013-05-23 12:23:18
K-OMS-2和铈K OMS2支持0.5wt%澳大利亚由双重起初水湿注入(DIWI)。DIWI包括第一注入步使用HAuCl4的解答(使用声处理)，跟随由Na2CO3 (1 M)的水溶液的加法，在恒定的超音波搅拌下。发生的固体一再洗涤了与氯化物撤除的蒸馏水，并且烘干在烤箱在12个h.表的1 110℃在这工作总结所有材料被综合的，以及半新的命名原则。
|
|
2013-05-23 12:24:58
K-OMS-2和铈K OMS 2支持0.5wt% Au由双重起初水湿注入 (DIWI)。 DIWI使用HAuCl4的解答包括第一注入步 (使用声处理)，跟随由碳酸钠的水溶液的加法 (1 M)，在恒定超音波搅动之下。 发生的固体在烤箱一再洗涤了与蒸馏水为氯化物撤除并且被烘干了在110℃为12 h。 表1在这工作总结所有材料被综合，以及半新的命名原则。
|
|
2013-05-23 12:26:38
0.5wt%Au K-OMS-2 和 Ce–K-OMS-2 上得到支持双起动水湿浸渍 （DIWI)。DIWI 包括使用解决方案的 HAuCl4 （使用超声处理），其次是另外的 Na2CO3 水溶液浸渍第一步 (1 M)，在恒定的超声搅拌下。由此产生的固体与氯去除蒸馏水反复洗，在 110 ℃ 烘箱中干燥为 12 h.表 1 总结了这项工作，在合成的所有材料，以及采用的命名法。
|
|
2013-05-23 12:28:18
0wt%的非盟支持K-OMS2和CE-K-2业务管理系统由双刚刚湿浸渍[diwi]。 diwi包括一个第一次受孕一步使用一个解决方案的使用haucl4[sonication],紧接着是一个水溶性解决方案的NA2CO3[1m],不断超声波搅动。 由此造成固体冲用蒸馏水反复的氯化物去除和干燥的烘箱中110°℃,12H。 表1总结了所有的材料综合在这项工作中,以及使用的术语。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区