求翻译：Under strong reducing conditions iron oxide was almost completely reduced and the slag phase solidified as a consequence thereof because FeO acts as a fluxing agent for high titania slags. Cr2O3, SiO2, MnO were also reduced to a high degree. Under weak reducing conditions a fully molten slag was stable as iron oxide wa是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Under strong reducing conditions iron oxide was almost completely reduced and the slag phase solidified as a consequence thereof because FeO acts as a fluxing agent for high titania slags. Cr2O3, SiO2, MnO were also reduced to a high degree. Under weak reducing conditions a fully molten slag was stable as iron oxide wa
问题补充： |
|
2013-05-23 12:21:38
在强还原条件下铁的氧化物几乎完全被降低，其炉渣相凝固的后果，因为FeO的高钛炉渣作为助熔剂。的Cr2O3，二氧化硅，氧化锰也降低到一个高度。在弱还原条件下完全熔融的炉渣是稳定的，如氧化铁，仅部分地减少。大的部分除去锰和一些氧化镁，通过气相由于其相当大的蒸汽压力。没有减少所施加的条件下，氧化铝。持续下降很容易实现，但超过90％（重量），使二氧化钛渣。％的二氧化钛与1700degreesc的液相线温度以上，与工业数据比较，实验结果表明在非均衡条件下，工业钛铁矿冶炼过程中操作。
|
|
2013-05-23 12:23:18
在强烈降低条件铁氧化物几乎完全是减少和渣凝固阶段,因为其后果的feo作为稀释剂的高来到Titania酒店这炉渣。 CR2O3,sio2,MNO也减少到一个高度。 减少薄弱的条件下充分熔融渣是稳定的,因为铁氧化物只是部分减少。 很大一部分的锰和一些含氧化镁,被通过气相由于%
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
|
|
2013-05-23 12:28:18
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区