求翻译：The PVdF ultrafine fiber prepared in Example 2-1 was put into a 4M aqueous sodium hydroxide aqueous solution maintained at about 70.degree. C. and prepared by dissolving which 0.25 mole tetrabutylammonium bromide was dissolved and maintained at about 70.degree. C., and defluorinated for about one hour, thereby preparin是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
The PVdF ultrafine fiber prepared in Example 2-1 was put into a 4M aqueous sodium hydroxide aqueous solution maintained at about 70.degree. C. and prepared by dissolving which 0.25 mole tetrabutylammonium bromide was dissolved and maintained at about 70.degree. C., and defluorinated for about one hour, thereby preparin
问题补充： |
|
2013-05-23 12:21:38
例2-1编写的聚偏氟乙烯超细纤维是投入保持在约70.degree一个4M的水氢氧化钠水溶液的解决方案。 C.和溶解0.25摩尔四丁基溴化准备解散，并保持在约70.degree。三，和脱氟约一小时，从而制订一个非熔融处理PVDF超细纤维。
|
|
2013-05-23 12:23:18
在编写PVDF超微细纤维的例子是以2比1力克放入一个4m水汽氢氧化钠水溶液维持在约70度。 C.及编制的解散,0.25胎四丁被解散,维持在约70度。 C.,和defluorinated,约一个小时,从而拟定一份非熔化PVDF对待超微细纤维。
|
|
2013-05-23 12:24:58
在例子准备的PVdF ultrafine纤维2-1中被放入4M含水氢氧化钠水溶液大约被维护在70.degree。 C. 并且通过0.25摩尔tetrabutylammonium溴化物大约被溶化并且被维护在70.degree的溶化准备。 C.和defluorinated大约一个小时，从而准备非熔化对待了PVdF ultrafine纤维。
|
|
2013-05-23 12:26:38
聚偏氟乙烯超细纤维编写的示例 2 1 月投入维持在大约 70.degree 4 M 水氢氧化钠水溶液。C.和准备溶的 0.25 摩尔丁基溴被解散，维持在大约 70.degree。C.和氟，约一个小时，从而准备非熔化处理聚偏氟乙烯超细纤维。
|
|
2013-05-23 12:28:18
例2-1编写的聚偏氟乙烯超细纤维是投入保持在约70.degree一个4M的水氢氧化钠水溶液的解决方案。 C.和溶解0.25摩尔四丁基溴化准备解散，并保持在约70.degree。三，和脱氟约一小时，从而制订一个非熔融处理PVDF超细纤维。
|