求翻译：Tafel Polarization curves of CRS in 0.5 M HCl in the absence and presence of different concentrations of DDTC at 30 C were shown in Fig. 2. As it can be seen that, the corrosion potentials obviously shifts to more negative direction while the cathodic curves are shifted to lower current density region compared to that 是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Tafel Polarization curves of CRS in 0.5 M HCl in the absence and presence of different concentrations of DDTC at 30 C were shown in Fig. 2. As it can be seen that, the corrosion potentials obviously shifts to more negative direction while the cathodic curves are shifted to lower current density region compared to that
问题补充： |
|
2013-05-23 12:21:38
CRS Tafel极化曲线c在0.5 M盐酸在缺乏和存在不同浓度DDTC 30见图。 2。因为它可以看到，明显的腐蚀电位更负方向移动，而阴极曲线空白的解决方案相比，电流密度较低的地区转移，这导致在icorr明显减少。这些现象清楚地表明，作为一个CRS阴极缓蚀剂在盐酸溶液，这是明显不同的抑制机制，其外的DDTC铜合金在NaCl作为一种混合型抑制剂[27]的DDTC行为。此外，阳极电流密度明显增加DDTC与空白溶液相比存在，表明可DDTC加速阳极反应。许多其他的研究中也观察到类似的结果[28-32]。 kocojan等人。 [33]和卡
|
|
2013-05-23 12:23:18
|
|
2013-05-23 12:24:58
|
|
2013-05-23 12:26:38
|
|